Pengaruh Penambahan Aluminium Oksida Terhadap Kekerasan dan Struktur Mikro Paduan Mg-Sn

  • Ayuda Darmawan Yulianto Jurusan Teknik Metalurgi, Universitas Jenderal Achmad Yani, Bandung, Indonesia
  • Muhammad Reza Parega Jurusan Teknik Metalurgi, Universitas Jenderal Achmad Yani, Bandung, Indonesia
  • Kusharjanto Suhirman Jurusan Teknik Metalurgi, Universitas Jenderal Achmad Yani, Bandung, Indonesia
  • Supono Adi Dwiwanto Jurusan Teknik Metalurgi, Universitas Jenderal Achmad Yani, Bandung, Indonesia
Keywords: Mg-Sn Alloy, Aluminium Oxide, Microstructure, Characteristic, Hardness

Abstract

This paper focused on hardness and microstructure of Mg-Sn alloy by Aluminium Oxide addition. Mg-Sn alloys were prepared by casting with the addition of Aluminium Oxide from 1% to 5%wt, then quenching to the water. The microstructure evolution and hardness were investigated. Based on hardness test result the hardness was increased. With 1% to 5% Aluminium Oxide addition, hardness increased from 22.9 BHN to 30.8 BHN. The highest hardness was in the addition of 5% Aluminium Oxide with 30.8 BHN. The result showed that increasing of Aluminium Oxide content resulted the globular and smaller grains.

Published
2018-12-31
How to Cite
Yulianto, A. D., Parega, M. R., Suhirman, K., & Dwiwanto, S. A. (2018). Pengaruh Penambahan Aluminium Oksida Terhadap Kekerasan dan Struktur Mikro Paduan Mg-Sn. Jurnal Metalurgi Dan Material Indonesia, 1(2), 07-11. Retrieved from https://www.materialmetalurgi.id/index.php/JMMI/article/view/16
Issue
Vol. 1 No. 2 (2018): Desember
Section
Artikel Ilmiah

Copyright (c) 2018 Ayuda Darmawan Yulianto, Muhammad Reza Parega, Kusharjanto Suhirman, Supono Adi Dwiwanto

Creative Commons License

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.